I'm not too sure how familiar you guys are with this but thought I'd ask whether anyone has attempted with that technique. As far as I know, this is done with chopped carbon fiber strands under high pressure. At least that's how Audemars Piguet does it with their watches. Recently, Lamborghini started using this method as well for their Sesto Elemento concept cars.  Does anybody have a clue whether this can be done in a home-based environment or you need hi-tech machinery?

I don't see how this could be used for structural parts though as you've lost any strength through fibre orientation, its basically pre preg CSM

Maybe the production technic is designed for strenght reliability (high pressure, ...)