Dezer	Dezer posted 7 Years Ago HOT Topic Details
Group: Forum Members Posts: 74, Visits: 1.8K	Hello friends, I was studying making 3D impression moulds and sealing with epoxy resin to make carbon fiber parts in the Wet Layup + Vacuum Bagging or Vacuum infusion process. Has anyone done any 3D impression mould? What better material for printing? The composites will be cured at room temperature. Thanks!
	Reply Like 11
Reply
Warren (Staff)	Warren (Staff) posted 7 Years Ago HOT Post Details
Group: Administrators Posts: 2.5K, Visits: 8.5K	Nice to see some natural fibres being used. How does it compare stiffness wise? Most natural fibres seem very poor compared to more advanced composite fibres - albeit usually the environmental credentials or different looks are usually more of a priority. Warren Penalver Easy Composites / Carbon Mods - Technical Support Assistant
	Reply Like 8

GO

Merge into selected topic...

Merge into merge target...

Merge into a specific topic ID...

Threaded View

Threaded View

Carbon Fiber Layup with Mould 3D Printer

Dezer - 7 Years Ago

ive done plenty of 3d printed tooling, if you are doing room temp wet lay then you can get away with PLA printed materials but you need to make sure they are properly sealed and released as Epoxy...

scottracing - 7 Years Ago

Thanks Scottracing, As it will be cured by ambient temperature the conventional materials will supply my needs well. Do you have any pictures of a 3D printed mould ? Thankful.

Dezer - 7 Years Ago

I just have some pictures of printed positive moulds on hand and thought i would share them. printed in PLA on a Prusa printer. second layer of spray filler sanded to 800 grid with tooling gel....

SleepingAwake - 7 Years Ago

This will help me a lot, for sure! Many thanks friend!

Dezer - 7 Years Ago

Hello! This looks very promising. I know it is old post but did not wanted to make new. Lester, can you comment on the finishing layers after 3D printed mold with filler is sanded? I suggest there....

vieteejais - 5 Years Ago

what layer height did you use on the PLA print? And did you sand it prior to the first coat of primer? The finished part looks brilliant, is that a flax/hemp material you made the part from?

scottracing - 7 Years Ago

I usually print with a Layer height of 0.15 to 0.2mm and give it a light sand to get rid of small bumps where a new layer started and any things like that. Then usually two coats of heavy filler and....

SleepingAwake - 7 Years Ago

0.15 layer height !!!! How many hours did it take you to print this bar mold ?

KostasBiz - 7 Years Ago

Many. But it's not like I was watching it...

SleepingAwake - 7 Years Ago

Nice to see some natural fibres being used. How does it compare stiffness wise? Most natural fibres seem very poor compared to more advanced composite fibres - albeit usually the environmental...

Warren (Staff) - 7 Years Ago

looks really good,we have been trialling some of the bcomp material at work and finding its not as good as it says on the tin,but i think for non structural applications like bodywork it should be...

scottracing - 7 Years Ago

one question : By printing my mold in PLA is it possible the exothermic reaction of curing resin to reach 60C or above that could soften my mold and ruin my cast? How can i suppress the rising of...

KostasBiz - 7 Years Ago

Yes, entirely possible but depends on the resin system and layer thickness. I make most of my molds with vacuum infusion and with those slow resins it is typically not an issue even for a very sturdy...

SleepingAwake - 7 Years Ago

Similar Topics

Post Quoted Reply

Reading This Topic

Login
Remember Me Reset Password Resend Validation Email Login	Facebook Google

Explore

Messages

Mentions

Search