Hi!

When molding carbon parts with high Vf (>50%) the fibres touching the mold are leaving a residue on my mold surface. I don't know why this is happening. I just bought easy lease release agent, but it also happened with wax (Partall). In fact I thought the Partall wax had aged so I bought Easy Lease thanks to this forum. But unfortunately no difference. The parts are demolding easy though with easy lease.

I have been using different curing processes: 24h room temp, 48h room temp, 24h 30 degrees C, 48h 30 degrees C. All with the same outcome: a residue on the mold. The molds are machined of PU toolingboard (Renshape) and polished to a mirror surface. Epoxies used are L + GL2 / S / L and EPH161 from R&G. When making a hand layup of one ply of carbon without compaction there is no printthrough and also no residue on the mold surface after demolding just like when using a gelcoat prior to the lay up.  So it looks like the problem is related to the compaction of the fibre or it maybe an epoxy problem.

Problems are gone! I guess my molds needed more coats of Easy Lease during break in time? Anyhow I found the masking tape test to be very useful. Thanks for all suggestions.