Also, report back with your results ! 

The problem with using other recommendations from other suppliers is you are up against different chemistry. Some will work or help others will make it worse.. I spent 6 months with one material getting different results from small changes and it has been a mixture of breather stack and ramp and dwell that I spent all my time on. Oddly some moulds need peel ply on the flange to bleed air and some don't. After a while you get to know which ones do and which ones don't. But the cure schedule never changes. You just need to make sure the oven is accurate with even temp top, bottom and middle or find a way to make sure you have the parts where the oven is working best. You may have to fine tune the controller and compensate for any differences. Mine is 2 degrees different from the thermocouple location to the centre of the oven.  Dwell times are important but I have found controlling ramp is actually more important than you think. Moulds may have different thickness so getting the moulds to all heat up within a margin that keeps them quite close will make all your parts cure consistently.

Its a bit of work to get your oven to be consistent but it is worth it... The SHD cure schedule is based on my findings and although I have not given them my breather stack info it is not to hide anything it is simply due to different moulds work differently so the only thing that will not change is the cure cycle.