From the XC110 datasheet,

CURED MECHANICAL PROPERTIES
Tests performed on XC110-C331T2-210(1250) laminate cured out-ofautoclave
Property Test Standard Units Result
Compressive strength BS EN ISO 14126 : 1999 MPa 483
Tensile strength BS EN ISO 527-4 : 1997 MPa 521
Tensile modulus BS EN ISO 527-4 : 1997 GPa 55.1
Flexural strength BS EN ISO 14125 : 1998 MPa 777
Flexural modulus BS EN ISO 14125 : 1998 GPa 46.7
Interlaminar shear strength BS EN 2563 : 1997 MPa 64.7
Tg Onset (DMA) ASTM 1-0003 Issue 3 °C 121
Tg Peak (DMA) ASTM 1-0003 Issue 3 °C 135

I understand the standards relating to the tests are as specified. Can I have further information (ie. thickness, number of ply(s), method of cure, cure temp & duration, etc..) regarding the specimens sent for these tests?