From the XC110 datasheet,
CURED MECHANICAL PROPERTIES Tests performed on XC110-C331T2-210(1250) laminate cured out-ofautoclave Property Test Standard Units Result Compressive strength BS EN ISO 14126 : 1999 MPa 483 Tensile strength BS EN ISO 527-4 : 1997 MPa 521 Tensile modulus BS EN ISO 527-4 : 1997 GPa 55.1 Flexural strength BS EN ISO 14125 : 1998 MPa 777 Flexural modulus BS EN ISO 14125 : 1998 GPa 46.7 Interlaminar shear strength BS EN 2563 : 1997 MPa 64.7 Tg Onset (DMA) ASTM 1-0003 Issue 3 °C 121 Tg Peak (DMA) ASTM 1-0003 Issue 3 °C 135
I understand the standards relating to the tests are as specified. Can I have further information (ie. thickness, number of ply(s), method of cure, cure temp & duration, etc..) regarding the specimens sent for these tests?
|