Anyone used/using Infuply?

http://www.cytec.com/products/infuply

I've just picked up a small-ish section to try out and wondered if anyone had any experience to share i.e. pro's and cons over using separate peel-ply and mesh?

I'm assuming that it doesn't tear so might not work great with complex moulds but interested to now how well it does come away and what kind of inner surface it leaves?

I have not used this stuff, It's probably just a flow medium and perforated release film bonded together to make the process a bit easier for large jobs like wind blades, boat hulls etc.

It's likely not so conformable as using separate layers of perf and flow medium so if your parts are small or detailed then this is probably not so good to use.