Matt Jones	M Matt Jones posted 7 Years Ago HOT Topic Details
M Group: Forum Members Posts: 6, Visits: 19	The technical sheet doesn't specify the pot life with a 2% ratio, can some one confirm? Also, if I reduce the ratio to 1.5% what will the pot life be and will that still give a complete cure? Thanks
	Reply Like 4
Reply
oekmont	oekmont posted 7 Years Ago HOT Post Details
Group: Forum Members Posts: 550, Visits: 27K	If it's too fast for your needs, you could buy polyester inhibitor. This can easily double or quadruple the geltime without risking uncuring resin.
	Reply Like 4

GO

Merge into selected topic...

Merge into merge target...

Merge into a specific topic ID...

Threaded View

Threaded View

Pattern coat High gloss pot life and catalyst ratio

Matt Jones - 7 Years Ago

I dont use the Easy Composites pattern coatings, but I do use Scott Bader Primecoat and Glosscoat which will be very very similar in their chemistry - so based on that, I would expect they will have....

Hanaldo - 7 Years Ago

Just the fact that you are making a mould means that everything you do with the pattern and the making your mould should be well cured! Having a proper cure is key to moulding and releasing well so....

Fasta - 7 Years Ago

Thanks both, but that doesn't answer the original question.

Matt Jones - 7 Years Ago

Did you find that it is too fast for application? The data sheet says 2% for usual 20 Degrees C, if you could reduce it to 1.5% as a test but then you should also compensate for the lesser catalyst%...

Fasta - 7 Years Ago

Assuming I'm close with my estimation for pot life at 2%, I'd estimate you'll be around a 40 to 45 minute pot life at 1.5%. If you're concerned, the easiest thing to do is just do your own gel test....

Hanaldo - 7 Years Ago

If it's too fast for your needs, you could buy polyester inhibitor. This can easily double or quadruple the geltime without risking uncuring resin.

oekmont - 7 Years Ago

Ok, to the original question: The high gloss coat has a pretty short pot life. To me it was like 10-15min. Could have been a summer day, but the temperature in my workshop never rises above 25°c. 1.5...

oekmont - 7 Years Ago

Thanks, I'd found the pattern coat was similarly 10-15 mins with at least a 60 sec stir, cutting it back to 1.75% seemed to make no difference. I'll go with 1.5% and be efficient, I think the data...

Matt Jones - 7 Years Ago