Hi guys...I'm getting variable results off my epoxy molds and am working thru possibilities (one being that I might need to look at temperatures when I import from the UK to New Zealand).
A general question for my understanding. Is it true that captured air on the mold surface is moved through the carbon cloth in the debulk step and then epoxy flows into the vacated space during the soak?
Or is air That will cause pinholes) being removed from the mold surface during the soak phase?...Cheers...Chris