What is the smallest radius corner you can successfully vacuum bag carbon finer around? 

It would be very hard if not impossible to quantify it. I have laid carbon around some very tight radius' (more than 90 degrees, easy) without issue. I think the more difficult task is having to lay the fibres over tight radius' that go in different directions, as this pulls the fibres all over the place and make it more likely to bridge.