Resin Composition and Mould Release

Talk Composites - The Forum for Advanced Composites

Back

Resin Composition and Mould Release

Author	Message
MohammadRiyaz	MohammadRiyaz posted 9 Years Ago HOT Topic Details
Group: Forum Members Posts: 1, Visits: 7	Hi, I am using these compounds for my resin as these are the only ones available: Epoxy Resin - (Bisphenol – A – Epichlorohydrin) Hardener - (3 – Amino Methyl – 3, 5, 5 –trimethylcyclohexylamine) What ratio should I use so as to achieve a strong part and a glossy finish? I tried (10:1) and (5:1), the part still seems to be quite weak. I tested with the (5:1) ratio and the overall viscosity of the mixture seems low and I get air bubbles inside the part. The part is made up of 25 layers of glass fibres (Woven) so it's solid. Its a layering procedure only. The mixture also does not produce any heat when combined together. The part also does not pop out of the mould and it takes a lot of hammering to get it out which damages the upper surface. I used a lot of Honey wax mould release for this as this was the only one available. The mould is just a hollow cavity of a part and I tried to layer the fibres using a stainless steel base below it. The resin still spreads on the whole stainless steel base when everything is cured but pops out well without effort due to wax release. I am quite new to this but I think with your advice I would be able to find a proper solution and share it with all of you. Thanks. Tags Epoxy resin Fiberglass hardener Wax
	Reply Like 3
Warren (Staff)	Warren (Staff) posted 9 Years Ago HOT Post Details
Group: Administrators Posts: 2.5K, Visits: 7.9K	You would really need to speak to the resin manufacturer to find out the correct ratio. It is not as simple to say resins containing x and y can use a ratio of b:c. The componants will likely be in different proportions and have different additives depending on the manufacturers blend. Warren Penalver Easy Composites / Carbon Mods - Technical Support Assistant
	Reply Like 2
Dravis	Dravis posted 9 Years Ago HOT Post Details
Group: Forum Members Posts: 592, Visits: 1.9K	The hardener and resin are most often a "matched pair" so you will usually not get good results when "mixing" hardener and resin from different manufacturers or even different products from the same manufacturer. Most "matched" Epoxy systems have a Hardener-to-Resin ratio of between 1:10 and 1:3, some specialist types may have 1:2 or 1:1, but that is usually coating types or "fillers" Some Epoxy "systems" are very forgiving in terms of the mixing ratio, and do not require great accuracy in getting the ratio correct, others are very "delicate" and require precision weighing of both Resin and Hardener. Also you really need to be sure of the ratio, is it by weight or volume?? Correctly cured epoxy resin will be very hard (normal laminating/infusion types) and quite brittle, when not being laminated or with added "filler" Some Coating types will be a bit "tough" or very slightly flexible. If you can not get the correct ratio from the manufacturer, you can do a controlled test, by mixing up small batches (in disposable plastic cups) and leaving them to cure at the exact same temperature/moisture and for the same time. Then test them. The proper ratio will be the one that produces the hardest, slightly brittle sample. (I would test 1:3, 1:4 and 1:5 by weight first, they are the most likely) "Sapere Aude"... Dare to KNOW! The written word is the only truly efficient vehicle for transmitting a complex concept from mind to mind... 103% of all people do not understand statistics... Do not adjust our mind, theres a fault in reality :-)
	Reply Like 3