Hi,
I have a question about a curing cycle for XC110. In the processing guide there are recommended controlled ramp-rate curing cycles, even extended soak cycle for heavier moulds. As I have also heavy aluminium mould, I will use extended cycle. Reaching temperatures is not problem. My problem is to keep the ramp-rate with my heavy alu mould. Is it a big problem when the temperature inside the mould has a slower ramp-rate than recommended if I keep the soak-/curing time the same? So, reaching 70°C will take instead of 50min for example 1,5h, than 6 hours soak...and the same for reaching 120°C...2 hours instead of 25min and then 1 hour curing.
Thanks for aswers!